The potential of a surface‐modified titanium implant with tetrapeptide for osseointegration enhancement

Syamsiah Syam, Chia Jen Wu, Wen Chien Lan, Keng Liang Ou, Bai Hung Huang, Yu Yeong Lin, Takashi Saito, Hsin Yu Tsai, Yen Chun Chuo, Ming Liang Yen, Chung Ming Liu, Ping Jen Hou

研究成果: 雜誌貢獻文章同行評審

3 引文 斯高帕斯(Scopus)

摘要

In this study, the innovative dip‐coating technique treated titanium (IDCT‐Ti) implant with tetrapeptide Gly‐Arg‐Gly‐Asp (GRGD) coating was investigated for its potential to enhance osseointegration. The L929 fibroblast cells were cultured in different concentrations of the GRGD (1%, 2%, and 5%). The cell viability was assessed through 3‐[4,5‐dimethylthiazol‐2‐yl]‐2,5‐ diphenyltetrazolium bromide (MTT) assay and live/dead staining. The surface topography and nano‐indentation were analyzed by atomic force microscopy. The hemocompatibility was evaluated via field‐emission scanning electron microscopy, while contact angle analysis was detected by a goniometer. Radiograph evaluation was determined by panoramic imaging. It was found that the cell growth increased and had a survival rate of more than 70% in 1% GRGD. The mortality of L929 increased with the higher concentration of GRGD. The IDCT‐Ti coated with 1% GRGD showed a nano‐surface with a Young’s modulus that was similar to human cortical bone, and it displayed greater red blood cell accumulations with abundant fibrin formation. As regards the wettability, the IDCT‐Ti coated with 1% GRGD was lower than the SLA (sandblasted, large‐grit, and acid‐etched) treated implant. The X‐ray image exhibited no bone loss around the implant at six months after placement. As a result, this study suggests that the IDCT‐Ti implant, coated with 1% GRGD, has a tremendous likeliness to enhance osseointegration.

原文英語
文章編號2616
期刊Applied Sciences (Switzerland)
11
發行號6
DOIs
出版狀態已發佈 - 3月 2 2021

ASJC Scopus subject areas

  • 材料科學(全部)
  • 儀器
  • 工程 (全部)
  • 製程化學與技術
  • 電腦科學應用
  • 流體流動和轉移過程

指紋

深入研究「The potential of a surface‐modified titanium implant with tetrapeptide for osseointegration enhancement」主題。共同形成了獨特的指紋。

引用此