The influence of cosolvents and in situ-forming hydroxyapatite on permeation characteristics of collagen films

Hsiu O. Ho, Chia Ming Liu, Ming Thau Sheu

研究成果: 雜誌貢獻文章同行評審

摘要

Collagen was processed into film in mixtures containing various ratios of water, propylene glycol, and ethanol. Hydroxyapatite (HAP) crystals were also introduced into collagen films by in-situ formation. Permeability studies were employed to characterize their influence on the permeation of various solutes through the collagen films with or without the presence of HAP. For a series of alkyl parabens and macromolecules, permeabilities across collagen films with and without the presence of HAP decreased with increasing chain length of alkyl parabens and molecular weight of macromolecules. There were significant alterations in permeabilities for alkyl parabens and macromolecules permeating through collagen films containing HAP. This is probably due to the introduction of HAP further modifying the network and the flexibility of collagen films, in turn affecting the permeation of solutes. However, results reveal that the influence of solvent mixtures that used to prepare collagen films on the permeation of various solutes through collagen films with and without HAP was similar. A linear correlation between the logarithm of permeability and the square of the radius of macromolecules was observed for permeation across collagen films without the presence of HAP. This relationship is similar to that for permeation through collagen films of different solvent mixtures.

原文英語
頁(從 - 到)437-448
頁數12
期刊Chinese Pharmaceutical Journal
54
發行號6
出版狀態已發佈 - 十二月 2002

ASJC Scopus subject areas

  • Bioengineering
  • Pharmaceutical Science

指紋 深入研究「The influence of cosolvents and in situ-forming hydroxyapatite on permeation characteristics of collagen films」主題。共同形成了獨特的指紋。

引用此