Synergistic effect in an Au-Ag alloy nanocatalyst: CO oxidation

Jun Hong Liu, Ai Qin Wang, Yu Shan Chi, Hong Ping Lin, Chung Yuan Mou

研究成果: 雜誌貢獻文章同行評審

355 引文 斯高帕斯(Scopus)

摘要

Au-Ag alloy nanoparticles supported on mesoporous aluminosilicate have been prepared by one-pot synthesis using hexadecyltrimethylammonium bromide (CTAB) both as a stabilizing agent for nanoparticles and as a template for the formation of mesoporous structure. The formation of Au-Ag alloy nanoparticles was confirmed by X-ray diffraction (XRD), ultraviolet-visible (UV-vis) spectroscopy, and transmission electron microscopy (TEM). Although the Au-Ag alloy nanoparticles have a larger particle size than the monometallic gold particles, they exhibited exceptionally high activity in catalysis for low-temperature CO oxidation. Even at a low temperature of 250 K, the reaction rate can reach 8.7 × 10-6 mol·gcat. -1·-1 at an Au/Ag molar ratio of 3/1. While neither monometallic Au@MCM-41 nor Ag@MCM-41 shows activity at this temperature, the Au-Ag alloy system shows a strongly synergistic effect in high catalytic activity. In this alloy system, the size effect is no longer a critical factor, whereas Ag is believed to play a key role in the activation of oxygen.

原文英語
頁(從 - 到)40-43
頁數4
期刊Journal of Physical Chemistry B
109
發行號1
DOIs
出版狀態已發佈 - 1月 13 2005
對外發佈

ASJC Scopus subject areas

  • 物理與理論化學
  • 表面、塗料和薄膜
  • 材料化學

指紋

深入研究「Synergistic effect in an Au-Ag alloy nanocatalyst: CO oxidation」主題。共同形成了獨特的指紋。

引用此