研究成果: 雜誌貢獻文章同行評審

摘要

Titanium dioxide is added into calcium phosphate bio-glass (CPG) to have crystalline phases of titanium phosphoric (TiP2O7) and calcium phosphoric (CaP2O7) on its surfaces. The bio-glass synthesis with the addition of titanium dioxide herein is denoted as TCPG. To elucidate their surface morphologies, both specimens of CPG and TCPG were immersed in Hanks' solution for two days before soaking in the mixed solutions of (NH4)2HPO4 and Ca(NO3) 2 at 70°. Crystalline layers of titanium phosphoric were observed on the surfaces of TCPG from immersing in Hanks' solution. After which calcium pyrophosphate appeared on the second step of soaking process from the calcium ion contained solutions. Due to the absence of crystalline phases on the surfaces of CPG specimen, it can be deduced that the addition of titania (TiO2) causes the hydroxyapatite formation on the surface of bio-glass.

原文英語
頁(從 - 到)389-394
頁數6
期刊Biomedical Engineering - Applications, Basis and Communications
19
發行號6
DOIs
出版狀態已發佈 - 12月 2007
對外發佈

ASJC Scopus subject areas

  • 生物物理學
  • 生物工程

指紋

深入研究「Surface morphologies on the addition of TiO2 to calcium phosphate bio-glass」主題。共同形成了獨特的指紋。

引用此