Surface-enhanced Raman scattering on a silver film-modified Au nanoparticle-decorated SiO2 mask array

Chi Ching Chang, Liang Yih Chen, Kuang Hsuan Yang, Qing Ye Chen, Yu Chih Liang, Shyr Yi Lin, Yu Chuan Liu

研究成果: 雜誌貢獻文章

3 引文 斯高帕斯(Scopus)

摘要

Nano-structured Ag and Au with well-defined localized surface plasmon resonance (LSPR) are most popularly employed in surface-enhanced Raman scattering (SERS)-related studies. Ag possesses the highest molar extinction coefficient in metals, resulting in a stronger SERS effect than that of Au. However, compared to Au, the serious decay of SERS enhancement in ambient laboratory air limits its reliable application. In this work, we develop a new strategy for preparing highly SERS-active Ag films deposited on Au nanoparticle (NP)-decorated SiO2 mask arrays based on electrochemical methods. The idea is derived from the underpotential deposition (UPD) of metals, which works on enhancing the SERS effect of underneath Au NPs as well as on reducing the decay of surface Ag films. Experimental results indicate that the SERS of Rhodamine 6G (R6G) absorbed on this developed array exhibits a higher intensity by ca. 30-fold, as compared with that of R6G absorbed on the Au NP-based array without the modification of Ag films. This strategy is also practically applicable to the trace detection of solutions containing calcium pyrophosphate dihydrate (CPPD), which is a common form of calcium crystals found in articular cartilage. In addition, aging (in an atmosphere of 50% relative humidity (RH) and 20% (v/v) O2 at 30°C for 60 day) of the SERS effect observed on this developed array is significantly depressed, which is comparable to that observed on the Au NP-based array without the modification of Ag films.
原文英語
頁(從 - 到)66096-66103
頁數8
期刊RSC Advances
5
發行號81
DOIs
出版狀態已發佈 - 七月 23 2015

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Chemistry(all)

指紋 深入研究「Surface-enhanced Raman scattering on a silver film-modified Au nanoparticle-decorated SiO<sub>2</sub> mask array」主題。共同形成了獨特的指紋。

  • 引用此