Strength and biocompatibility of heparin-based calcium phosphate cement grafted with ferulic acid

Kai Chi Chang, Jian Chih Chen, I. Tse Cheng, Ssu Meng Haung, Shih Ming Liu, Chia Ling Ko, Ying Sui Sun, Chi Jen Shih, Wen Cheng Chen

研究成果: 雜誌貢獻文章同行評審

3 引文 斯高帕斯(Scopus)


The biomimetic synthesis of carbonated apatites by biomolecule-based templates is a promising way for broadening apatite applications in bone tissue regeneration. In this work, heparin was used as an organic template to prepare uniform carbonate-based apatite nanorods (CHA) and graft ferulic acid (F-CHA) for enhanced bone mineralization. Next, by combining calcium phosphate cement (CPC) with different F-CHA/CPC ratios, a new type of injectable bone cement combined with F-CHA bioactive apatite was developed (CPC + F-CHA). The physicochemical properties, biocompatibility, and mineralization potential of the CPC + F-CHA composites were determined in vitro. The experimental results confirmed the preparation of highly biocompatible CHA and the compatibility of F-CHA with CPC. Although CPC + F-CHA composites with F-CHA (2.5 wt%, 5 wt%, and 10 wt%) showed a significant reduction in compressive strength (CS), compositing CPC with 10 wt% F-CHA yielded a CS suitable for orthopedic repair (CS still larger than 30 MPa). Spectroscopic and phase analyses revealed that the phase of the hydrothermally synthesized CHA product was not modified by the heparin template. Injection and disintegration tests indicated that the CPC + F-CHA composites have good biocompatibility even at 10 wt% F-CHA. D1 osteoprogenitor cells were cultured with the composites for 7 days in vitro, and the CPC + 10%F-CHA group demonstrated significantly promoted cell mineralization compared with other groups. Given these results, the use of over 10% F-CHA in CPC composites should be avoided if the latter is to be applied to load-bearing areas. A stress-shielding device may also be recommended to stabilize these areas. These newly developed biocompatible CPC + F-CHA have great potential as osteoconductive bone fillers for bone tissue engineering.
出版狀態已發佈 - 7月 2021

ASJC Scopus subject areas

  • 化學 (全部)
  • 聚合物和塑料


深入研究「Strength and biocompatibility of heparin-based calcium phosphate cement grafted with ferulic acid」主題。共同形成了獨特的指紋。