Quantitative correlation of the effects of crystallinity and additives on nanomorphology and solar cell performance of isoindigo-based copolymers

Chih Yu Chang, Yu Ching Huang, Cheng Si Tsao, Chien An Chen, Chun Jen Su, Wei Fang Su

研究成果: 雜誌貢獻文章同行評審

摘要

The high power conversion efficiency of bulk heterojunction (BHJ) polymer solar cells can be achieved from either low crystallinity (P3TI) or high crystallinity (P6TI) of isoindigo-based donor-acceptor alternating copolymers blended with PC 71 BM by controlling nanophase separation using additives. P3TI shows similar device performance regardless of the type of additives, while P6TI is significantly affected by whether the additive is aliphatic or aromatic. To understand the interplays of crystallinity of polymers and the type of additive on the formation of nanomorphology of BHJ, we employed the simultaneous grazing-incidence small- and wide-angle X-ray scattering (GISAXS and GIWAXS) technique to perform the quantitative investigation. By incorporating additives, the PC 71 BM molecules can be easily intercalated into the P3TI polymer-rich domain and the size of the PC 71 BM clusters is reduced from about 24 nm to about 5 nm by either aliphatic 1,8-diiodooctane (DIO) or aromatic 1-chloronaphthalene (CN). On comparison, it is found to be more difficult for PC 71 BM molecules to be intercalated into the highly crystalline P6TI dense domain, and the PC 71 BM molecules have a higher tendency to be self-aggregated, which results in a larger size of PC 71 BM clusters of about 58 nm. The clusters can be reduced to about 7 nm by DIO and 13 nm by CN. The presence of crystallites in the P6TI domain can interact with the additive to tailor the crystallization of PC 71 BM clusters to a size similar to that of P6TI crystallites (∼12 nm) and form a connected network for efficient charge transportation. Thus, the power conversion efficiency of P6TI:PC 71 BM reaches its maximum of 7.04% using aromatic CN additives. This is a new finding of the effect of crystallinity, which is not observed in the common low crystalline donor-acceptor alternating copolymers such as PTB7. Our results provide a useful guideline to manipulate the desired morphology of BHJ films constructed from alternating copolymer with different crystallinity, which is critical for achieving high power conversion efficiency of solar cells.
原文英語
頁(從 - 到)23515-23523
頁數9
期刊Physical Chemistry Chemical Physics
19
發行號34
DOIs
出版狀態已發佈 - 一月 1 2017
對外發佈Yes

ASJC Scopus subject areas

  • Physics and Astronomy(all)
  • Physical and Theoretical Chemistry

指紋 深入研究「Quantitative correlation of the effects of crystallinity and additives on nanomorphology and solar cell performance of isoindigo-based copolymers」主題。共同形成了獨特的指紋。

引用此