Preparation of Mg-Y-Cu bulk metallic glass by high energy rail milling

P. Y. Lee, M. C. Kao, C. K. Lin

研究成果: 雜誌貢獻文章同行評審

摘要

We have studied the amorphization behavior of Mg85-xY 15Cux (x=20~40) alloy powders synthesized by high energy ball milling technique. The as-milled powders were mainly amorphous after 1 0 hours of milling. The thermal stability o f these Mg85-xYi 15Cux glassy powders was investigated by differential scanning calorimeter (DSC). The ranges of Tg ,Tx and ΔTX are around 430-459K, 467-497K, and 30-46K, respectively. Mg61Y15Cu24bulk metallic glass with nanocrystalline precipitates homogeneously embedded in a highly dense glassy matrix was successfully prepared by vacuum hot pressing. It was found that the applied pressure during consolidation could enhance the thermal stability and prolong the existence of amorphous phase inside Mg61Y 15Cu24 powders.
原文英語
頁(從 - 到)97-100
頁數4
期刊Journal of Metastable and Nanocrystalline Materials
24-25
DOIs
出版狀態已發佈 - 2005
對外發佈

ASJC Scopus subject areas

  • 材料科學(雜項)
  • 材料科學(全部)
  • 凝聚態物理學
  • 物理與理論化學

指紋

深入研究「Preparation of Mg-Y-Cu bulk metallic glass by high energy rail milling」主題。共同形成了獨特的指紋。

引用此