Preparation and thermal stability of mechanically alloyed Ni-Zr-Ti-Y amorphous powders

Chung Kwei Lin, Chien Chung Wang, Rong Ruey Jeng, Yu Lom Lin, Chien Hung Yeh, Jinn P. Chu, Pee Yew Lee

研究成果: 雜誌貢獻文章同行評審

6 引文 斯高帕斯(Scopus)

摘要

In the current study, amorphous Ni67-xZr10Ti 23Yx alloy powders were synthesized by mechanical alloying technique. The mechanically alloyed powders were amorphous, after 5 h of milling, at compositions of Ni67-xZr10Ti 23Yx (x=0-12). The amorphization behavior of Ni 59Zr10Ti23Y8 was examined in details. The conventional X-ray diffraction and synchrotron EXAFS results confirm that the fully amorphous powders formed after 5 h of milling. The thermal stability of the Ni67-xZr10Ti23Y x amorphous powders was investigated by differential scanning calorimeter. As the results demonstrated, the amorphous powders with low yttrium concentration (x=0-6) or high yttrium concentration (x=12) exhibit no glass transition behavior. However, the Ni67-xZr10Ti 23Yx (x=7-10) amorphous powders were found to exhibit a wide supercooled liquid region before crystallization.
原文英語
頁(從 - 到)1011-1017
頁數7
期刊Intermetallics
12
發行號7-9 SPEC. ISS.
DOIs
出版狀態已發佈 - 七月 2004
對外發佈

ASJC Scopus subject areas

  • 化學 (全部)
  • 材料力學
  • 機械工業
  • 金屬和合金
  • 材料化學

指紋

深入研究「Preparation and thermal stability of mechanically alloyed Ni-Zr-Ti-Y amorphous powders」主題。共同形成了獨特的指紋。

引用此