Photoluminescent Evolution Induced by Structural Transformation Through Thermal Treating in the Red Narrow-Band Phosphor K2GeF6:Mn4+

Ling Ling Wei, Chun Che Lin, Yi Ying Wang, Mu Huai Fang, Huan Jiao, Ru Shi Liu

研究成果: 雜誌貢獻文章同行評審

120 引文 斯高帕斯(Scopus)

摘要

This study explored optimal preparation conditions for K2GeF6:Mn4+ red phosphors by using chemical coprecipitation method. The prepared hexagonal P3m1 K2GeF6:Mn4+ exhibited efficient red emission, high color purity, good Mn4+ concentration stability, and low thermal quenching. Structural evolution from hexagonal P3m1 to P63mc and then P63mc to cubic Fm3m occurred after thermal treatment at approximately 400 and 500°C, respectively. Hexagonal P63mc phase showed an obvious zero phonon line peak at 621 nm, whereas cubic Fm3m phase showed no red emission. Yellowish K2GeF6:Mn4+ with both hexagonal P3m1 and P63mc symmetries are promising commercial red phosphors for white light-emitting diodes. (Figure Presented)
原文英語
頁(從 - 到)10656-10659
頁數4
期刊ACS Applied Materials and Interfaces
7
發行號20
DOIs
出版狀態已發佈 - 五月 27 2015
對外發佈

ASJC Scopus subject areas

  • 材料科學(全部)

指紋

深入研究「Photoluminescent Evolution Induced by Structural Transformation Through Thermal Treating in the Red Narrow-Band Phosphor K<sub>2</sub>GeF<sub>6</sub>:Mn<sup>4+</sup>」主題。共同形成了獨特的指紋。

引用此