Optimal process parameters for 3Y-TZP/TiN conductive polycrystal by Taguchi method

Cui Feng Wang, Shi Yung Chiou, Keng Liang Ou, Zhang Ting Cai

研究成果: 雜誌貢獻文章同行評審

3 引文 斯高帕斯(Scopus)

摘要

For the manufacturing of 3mol% Yttria-tetragonal Zirconia polycrystal (3Y-TZP) with 30wt% of Titanium Nitride (TiN) (3Y-TZP/TiN) powders, Taguchi method was used to selected the process parameters including sintering step variation, crushing time of TiN powder, the first step sintering duration and second step sintering temperature to be the controlling factors. The characterization features of sintered samples such as fracture toughness, flexural strength, hardness, relative density and electric resistance were explored through L 9 orthogonal array. By analysis of variance (ANOVA), the optimal parameter settings for each response factor were obtained and tested through confirmation experiments. The results indicate that the optimal process parameters contain 8 h crushing time of TiN powder, two - steps sintering processes including the 1450°C temperature with no duration for the first step and 1150°C temperature and 20 h duration for the second step, and the average flexural strength of 736.75 MPa and fracture toughness of 7.545 MPa(m 1/2 are obtained. In addition, the degree of the process parameter effects on the sintered samples is found in the series of the sintering duration of the first step, sintering step variation, size of TiN particles and the sintering temperature of the second step. Meanwhile, fracture toughness depends significantly on the ratio of tetragonal phase to monoclinic phase and attends to be 9.275 MPa·m 1/2 when the ratio is getting to the maximum. The average electric resistance for 3Y-TZP/ TiN is measured to be 3.26 mΩ·cm. These samples can be electric-discharge machined.

原文英語
頁(從 - 到)529-535
頁數7
期刊Wuji Cailiao Xuebao/Journal of Inorganic Materials
27
發行號5
DOIs
出版狀態已發佈 - 五月 2012

ASJC Scopus subject areas

  • 材料科學(全部)
  • 無機化學

指紋

深入研究「Optimal process parameters for 3Y-TZP/TiN conductive polycrystal by Taguchi method」主題。共同形成了獨特的指紋。

引用此