New developments in the growth of 4 Angstrom carbon nanotubes in linear channels of zeolite template

Qihong Chen, Zhe Wang, Yuan Zheng, Wu Shi, Dingdi Wang, Yi Chia Luo, Bing Zhang, Jianming Lu, Haijing Zhang, Jie Pan, Chung Yuan Mou, Zikang Tang, Ping Sheng

研究成果: 雜誌貢獻文章同行評審

9 引文 斯高帕斯(Scopus)

摘要

We report new developments on the chemical vapor deposition growth of 0.4 nm single-walled carbon nanotubes (SWCNTs) inside the linear channels of the aluminophosphate zeolite, AlPO4-5 (AFI), single crystals (0.4 nm-SWCNT@AFI). Ethylene (C2H4) and carbon monoxide (CO) were used as the feedstock. Polarized Raman spectroscopy was used to analyze the structure and quality of SWCNTs, both the radial breathing mode and G-band are much clearer and stronger than the samples grown by the old process which used template tripropylamine molecules for growing SWCNT@AFI. From the Raman spectra, it is clearly seen that the RBM is composed of two peaks at 535 and 551 cm -1. By using the pseudopotential module in Material Studio to calculate the Raman lines, the 535 cm-1 peak is attributed to the (5,0) SWCNTs and the 551 cm-1 peak to the (3,3) SWCNTs. The abundance of (4,2) is relatively small. Thermal gravity analysis showed that while the samples grown by CO display less than 1 wt% of carbon, for the samples heated in C2H4 atmosphere the weight percentage of SWCNTs is around 10%, which implies ∼30% of the AFI channels are occupied with SWCNTs, a significant increase compared with the previous samples.

原文英語
頁(從 - 到)401-409
頁數9
期刊Carbon
76
DOIs
出版狀態已發佈 - 9月 2014
對外發佈

ASJC Scopus subject areas

  • 化學 (全部)
  • 材料科學(全部)

指紋

深入研究「New developments in the growth of 4 Angstrom carbon nanotubes in linear channels of zeolite template」主題。共同形成了獨特的指紋。

引用此