Nanostructured hydroxyapatite coatings on NiTi shape memory alloys by ultrasonic mechanical coating and armouring

Ming Hong Lin, Fang Yu Fan, Cheng Hsien Kuo, Liang Wei Lin, Kuang Kuo Wang, Chin Fu Chen, Yan Hsiung Wang, Shih Fu Ou

研究成果: 雜誌貢獻文章同行評審

摘要

Mechanical energy-induced deposition on NiTi shape memory alloys (SMAs) is difficult to accomplish due to the pseudoelasticity of NiTi SMAs. In this study, a high-frequency ball-bombardment method called ultrasonic mechanical coating and armouring (UMCA) is introduced to synthesize a hydroxyapatite (HA)-containing coating on a NiTi SMA. The effects of treatment duration, Ti addition, and ball-to-powder ratio on the HA content of the coating are investigated. Results show that the HA content of the coating largely increased during the initial 10 s and decreased with further ball-bombardment. The addition of Ti powder into the chamber assisted HA anchoring on the NiTi SMA surface. Using a ball-to-powder ratio of 1:1 induced the highest HA content on the NiTi SMA as compared to the 1:2 and 2:1 ratios. Coating consisting of 10–50 nm nanoparticles of HA and Ti formed under localized compressive forces were induced through shot collisions. The bombardment also created a local amorphous structure of the NiTi SMA near the coating/NiTi SMA interface. Laser annealing induced oxidation of the coating, which improved the coating adhesion and corrosion resistance of the NiTi SMA in Hank's balanced salt solution.

原文英語
文章編號127998
期刊Surface and Coatings Technology
431
DOIs
出版狀態已發佈 - 2月 15 2022

ASJC Scopus subject areas

  • 化學 (全部)
  • 凝聚態物理學
  • 表面和介面
  • 表面、塗料和薄膜
  • 材料化學

指紋

深入研究「Nanostructured hydroxyapatite coatings on NiTi shape memory alloys by ultrasonic mechanical coating and armouring」主題。共同形成了獨特的指紋。

引用此