Manufacturing and characterization of NiTi alloy with functional properties by selective laser melting

Shih Fu Ou, Bou Yue Peng, Yi Cheng Chen, Meng Hsiu Tsai

研究成果: 雜誌貢獻文章同行評審

19 引文 斯高帕斯(Scopus)

摘要

In this study, an optimal selective laser melting (SLM) process for manufacturing dense NiTi alloy with pseudoelasticity and shape-memory capability was proposed. The microstructure, phase-transformation temperature, shape memory capability, and pseudoelasticity were investigated by scanning electron microscopy, X-ray diffraction, differential scanning calorimetry, and bending and tensile tests. NiTi powder with a particle size > 45 µm was selected for the subsequent SLM process, because it exhibited a Ni/Ti ratio of ~1 and a lower oxygen content than powders with smaller particle sizes. A thin-walled disk (0.48 mm thick) and cuboid samples (5 mm thick) were prepared for investigating the variation in the homogeneity of the microstructure. The thin-walled SLM-NiTi sample exhibited a marginally inhomogeneous microstructure between layers, and defects existed in the previously formed side. The cuboid SLM-NiTi sample was fabricated without undesirable secondary phases, and it exhibited a 100% shape-recovery rate under 2% bending strain and completely pseudoelastic under 3% strain. Also, the SLM-NiTi exhibited lower phase-transformation temperatures and a broader phase-transformation range than the original NiTi. The phase-transformation range can be reduced by annealing.
原文英語
文章編號342
期刊Metals
8
發行號5
DOIs
出版狀態已發佈 - 五月 11 2018

ASJC Scopus subject areas

  • 材料科學(全部)

指紋

深入研究「Manufacturing and characterization of NiTi alloy with functional properties by selective laser melting」主題。共同形成了獨特的指紋。

引用此