Influence of hydrolytic degradation on the surface properties of poly-5d/95l-lactide resorbable bone plates

Hsin Tai Hu, Tsai Chin Shin, Sheng Yang Lee, Chien Chung Chen, Jen Chang Yang

研究成果: 雜誌貢獻文章同行評審

10 引文 斯高帕斯(Scopus)

摘要

This study explores in vitro aging effects on the surface properties of resorbable PLA95 (poly-5d/95l-lactide) bone plates. The in vitro degradation of injection molded PLA95 bone plates was undertaken by soaking them in a PBS solution. Specimens were harvested at 0, 4, 6, 8, 12, 20, and 26 weeks. After each in vitro aging period, the surface morphology, viscosity, chemical structure, wettability, and thermal properties of the PLA95 bone plates were examined by scanning electron microscopy (SEM), capillary viscometers, attenuated total reflection fourier transform infrared spectroscopy (ATR-FTIR), contact angle, and modulated differential scanning calorimetry (MDSC), respectively. The surface morphology of aged PLA95 bone plates exhibited bulk erosion. As hydrolysis progressed, the inherent viscosity (I.V.) of the PLA95 plates gradually decreased from 0.83 ± 0.01 dL/g at week 0-0.46 ± 0.03 dL/g at week 26. However, the absorbance peak intensity ratio between δas CH3 (A1452 cm-1) and ν CO (A1750 cm-1) and the contact angle reveal different tendencies than that of molecular weight, which decreases. The contact angle of the PLA95 plates decreased until week 4, increased until week 8, and subsequently decreased again. Peak separation analysis reveals that the equilibrium part of the modulated DSC overlapped curves exhibit triple endothermic peaks. Over time, in vitro degradation changes the position and area of the individual peaks. After different time periods of degradation, the variation of wettability shows a tendency similar to the change of PLA95 plates crystallinity; the intensity ratio of A1452 cm -1 and A1750 cm-1 (δ as CH3/ν CO) absorbance peaks varied like the ratio of β/α-crystal heat of fusion. Results also show a similarity in the degradation time dependence in MDSC, contact angle, and ATR-FTIR measurements. During the in vitro aging process, the breakdown and subsequent recrystallization of PLA95 molecular chains might be attributed to a progressive change in wettability and the molecular conformation between δas CH3 and ν CO.
原文英語
頁(從 - 到)1522-1529
頁數8
期刊Polymer Degradation and Stability
96
發行號8
DOIs
出版狀態已發佈 - 八月 2011

ASJC Scopus subject areas

  • Polymers and Plastics
  • Materials Chemistry
  • Mechanics of Materials
  • Condensed Matter Physics

指紋 深入研究「Influence of hydrolytic degradation on the surface properties of poly-5d/95l-lactide resorbable bone plates」主題。共同形成了獨特的指紋。

引用此