Hydrothermal Synthesis of Co3O4/ZnCo2O4Core-Shell Nanostructures for High-Performance Supercapacitors

En Syuan Lin, Feng Sheng Chao, Chen Jui Liang, Chi Jung Chang, Alex Fang, Chung Kwei Lin, Yu Cheng Chang, Chien Yie Tsay, Jerry J. Wu, Chin Yi Chen

研究成果: 雜誌貢獻文章同行評審

摘要

Supercapacitive properties of Co/ZnCo oxide composite with a core-shell nanostructure (Co3O4/ZnCo2O4) prepared directly onto a nickel foam substrate by a two-step hydrothermal method were investigated. The synthesized core-shell structure consisted of some ~40-100 nm in thick flaky ZnCo2O4 deposits coated onto the surface of Co3O4 nanorods measuring ~150 nm in diameter. The specific capacitance value of the Co3O4/ZnCo2O4 core-shell nanostructure synthesized by hydrothermal at 130 °C for a ZnCo2O4 deposition time of 2 h can attain 1804 F g-1 at a scan rate of 5 mV s-1. Furthermore, the core-shell structured electrode still exhibited a relatively good capacitance retention of more than 93% after 3000 CV cycles due to the superior structural support of Co3O4 scaffolds. The Co3O4/ZnCo2O4 core-shell structure exhibits excellent electrochemical performances and, as such, is one of the more promising active materials in pseudocapacitor applications.

原文英語
文章編號123502
期刊Journal of the Electrochemical Society
168
發行號12
DOIs
出版狀態已發佈 - 12月 2021

ASJC Scopus subject areas

  • 電子、光磁材料
  • 可再生能源、永續發展與環境
  • 表面、塗料和薄膜
  • 電化學
  • 材料化學

指紋

深入研究「Hydrothermal Synthesis of Co3O4/ZnCo2O4Core-Shell Nanostructures for High-Performance Supercapacitors」主題。共同形成了獨特的指紋。

引用此