Hydrogen storage properties of (Mg2Ni)100-xAgx powder prepared by mechanical alloying

Jin Yi Chen, Xian Ke Lin, Zhong Kui Lin, Pei Yao Li

研究成果: 雜誌貢獻文章

摘要

In many hydrogen storage methods, metal hydrides proposed to have some advantages such as greater volumetric efficiency, relatively low pressure, and high safety issue have attracted many R and D interests. Among a number of alloys, A2B type Mg2Ni intermetallic alloy due to its high hydrogen absorption capacity, lightweight and low cost is considered as a promising candidate for hydrogen storage applications. In the present study, an intermetallic powder with a desired composition of (Mg2Ni)100-xAgx (x = 0, 1.0 and 5.0) was directly prepared by mechanical alloying from pure Mg, Ni and Ag elemental powders under an inert gas. The structural transformations of as-milled powder mixtures in varied milling times were examined by X-ray diffraction (XRD) technique. The hydrogen storage kinetics, pressure-composition-temperature (P-C-T) curves and thermal analysis of 15 h milled Mg2Ni / Ag powders were evaluated. The experimental results showed that the 15 h as-milled powders were identified as a nanocrystalline mixture of Mg2Ni, Mg and Ni. Silver addition significantly improved the hydrogen absorption capacity of Mg2Ni, revealing that the absorbed hydrogen content and reversible hydrogen content at 350 °C were increased from 3.14 to 3.83%(ω) and from 2.40 to 3.0%(ω), respectively, for the 15 h milled Mg2Ni powder at silver content of 1.0%.
原文英語
頁(從 - 到)258-262
頁數5
期刊Guocheng Gongcheng Xuebao/The Chinese Journal of Process Engineering
6
發行號SUPPL. 2
出版狀態已發佈 - 十二月 2006
對外發佈Yes

ASJC Scopus subject areas

  • Chemical Engineering(all)

指紋 深入研究「Hydrogen storage properties of (Mg<sub>2</sub>Ni)<sub>100-x</sub>Ag<sub>x</sub> powder prepared by mechanical alloying」主題。共同形成了獨特的指紋。

  • 引用此