Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure

Shin Mou Wu, Hao En Hung, Chi Hsing Hsieh, Yin Chih Lin, Li Chun Wang, Yi Ting Tsai, Chun Che Lin, Ru Shi Liu

研究成果: 雜誌貢獻文章

4 引文 (Scopus)

摘要

Firing temperature and gas pressure effect of synthesizing Sr2Si5N8:Eu2+ were investigated. The emission intensity is positively correlated with the firing temperature under 0.1 and 0.5 MPa gas pressure. The Sr2Si5N8:Eu2+ with the highest emission intensity was found at 1700°C and 1980°C under 0.1 and 0.5 MPa gas pressure, respectively. Although the maximum emission intensity of Sr2Si5N8:Eu2+ obtained under 0.5 MPa gas pressure condition is higher than that under 0.1 MPa. The Sr2Si5N8:Eu2+ synthesized under 0.5 MPa gas pressure in the temperature range from 1600°C to 1800°C have lower emission intensities than that synthesized under 0.1 MPa indicating that the melting of Sr3N2 is an important step for the formation of Sr2Si5N8:Eu2+. Moreover, the Sr2Si5N8:Eu2+ undergoes phase transition into SrSi6N8:Eu2+ completely after elongating the heating duration to 6 h at 1980°C under 0.5 MPa gas pressure. The same feature was observed under 0.1 MPa gas pressure after firing 8 h at 1750°C. Different heating durations led to different degrees of phase transition.
原文英語
頁(從 - 到)2662-2669
頁數8
期刊Journal of the American Ceramic Society
98
發行號8
DOIs
出版狀態已發佈 - 八月 1 2015
對外發佈Yes

指紋

Gases
Temperature
Phase transitions
Heating
Pressure effects
Melting

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

引用此文

Wu, S. M., Hung, H. E., Hsieh, C. H., Lin, Y. C., Wang, L. C., Tsai, Y. T., ... Liu, R. S. (2015). Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure. Journal of the American Ceramic Society, 98(8), 2662-2669. https://doi.org/10.1111/jace.13646

Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure. / Wu, Shin Mou; Hung, Hao En; Hsieh, Chi Hsing; Lin, Yin Chih; Wang, Li Chun; Tsai, Yi Ting; Lin, Chun Che; Liu, Ru Shi.

於: Journal of the American Ceramic Society, 卷 98, 編號 8, 01.08.2015, p. 2662-2669.

研究成果: 雜誌貢獻文章

Wu, Shin Mou ; Hung, Hao En ; Hsieh, Chi Hsing ; Lin, Yin Chih ; Wang, Li Chun ; Tsai, Yi Ting ; Lin, Chun Che ; Liu, Ru Shi. / Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure. 於: Journal of the American Ceramic Society. 2015 ; 卷 98, 編號 8. 頁 2662-2669.
@article{b121793f3b854b6ab797cc669880e039,
title = "Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure",
abstract = "Firing temperature and gas pressure effect of synthesizing Sr2Si5N8:Eu2+ were investigated. The emission intensity is positively correlated with the firing temperature under 0.1 and 0.5 MPa gas pressure. The Sr2Si5N8:Eu2+ with the highest emission intensity was found at 1700°C and 1980°C under 0.1 and 0.5 MPa gas pressure, respectively. Although the maximum emission intensity of Sr2Si5N8:Eu2+ obtained under 0.5 MPa gas pressure condition is higher than that under 0.1 MPa. The Sr2Si5N8:Eu2+ synthesized under 0.5 MPa gas pressure in the temperature range from 1600°C to 1800°C have lower emission intensities than that synthesized under 0.1 MPa indicating that the melting of Sr3N2 is an important step for the formation of Sr2Si5N8:Eu2+. Moreover, the Sr2Si5N8:Eu2+ undergoes phase transition into SrSi6N8:Eu2+ completely after elongating the heating duration to 6 h at 1980°C under 0.5 MPa gas pressure. The same feature was observed under 0.1 MPa gas pressure after firing 8 h at 1750°C. Different heating durations led to different degrees of phase transition.",
author = "Wu, {Shin Mou} and Hung, {Hao En} and Hsieh, {Chi Hsing} and Lin, {Yin Chih} and Wang, {Li Chun} and Tsai, {Yi Ting} and Lin, {Chun Che} and Liu, {Ru Shi}",
year = "2015",
month = "8",
day = "1",
doi = "10.1111/jace.13646",
language = "English",
volume = "98",
pages = "2662--2669",
journal = "Journal of the American Ceramic Society",
issn = "0002-7820",
publisher = "Wiley-Blackwell",
number = "8",

}

TY - JOUR

T1 - Formation of Sr2Si5N8:Eu2+ and Its Transformation to SrSi6N8:Eu2+ Controlled by Temperature and Gas Pressure

AU - Wu, Shin Mou

AU - Hung, Hao En

AU - Hsieh, Chi Hsing

AU - Lin, Yin Chih

AU - Wang, Li Chun

AU - Tsai, Yi Ting

AU - Lin, Chun Che

AU - Liu, Ru Shi

PY - 2015/8/1

Y1 - 2015/8/1

N2 - Firing temperature and gas pressure effect of synthesizing Sr2Si5N8:Eu2+ were investigated. The emission intensity is positively correlated with the firing temperature under 0.1 and 0.5 MPa gas pressure. The Sr2Si5N8:Eu2+ with the highest emission intensity was found at 1700°C and 1980°C under 0.1 and 0.5 MPa gas pressure, respectively. Although the maximum emission intensity of Sr2Si5N8:Eu2+ obtained under 0.5 MPa gas pressure condition is higher than that under 0.1 MPa. The Sr2Si5N8:Eu2+ synthesized under 0.5 MPa gas pressure in the temperature range from 1600°C to 1800°C have lower emission intensities than that synthesized under 0.1 MPa indicating that the melting of Sr3N2 is an important step for the formation of Sr2Si5N8:Eu2+. Moreover, the Sr2Si5N8:Eu2+ undergoes phase transition into SrSi6N8:Eu2+ completely after elongating the heating duration to 6 h at 1980°C under 0.5 MPa gas pressure. The same feature was observed under 0.1 MPa gas pressure after firing 8 h at 1750°C. Different heating durations led to different degrees of phase transition.

AB - Firing temperature and gas pressure effect of synthesizing Sr2Si5N8:Eu2+ were investigated. The emission intensity is positively correlated with the firing temperature under 0.1 and 0.5 MPa gas pressure. The Sr2Si5N8:Eu2+ with the highest emission intensity was found at 1700°C and 1980°C under 0.1 and 0.5 MPa gas pressure, respectively. Although the maximum emission intensity of Sr2Si5N8:Eu2+ obtained under 0.5 MPa gas pressure condition is higher than that under 0.1 MPa. The Sr2Si5N8:Eu2+ synthesized under 0.5 MPa gas pressure in the temperature range from 1600°C to 1800°C have lower emission intensities than that synthesized under 0.1 MPa indicating that the melting of Sr3N2 is an important step for the formation of Sr2Si5N8:Eu2+. Moreover, the Sr2Si5N8:Eu2+ undergoes phase transition into SrSi6N8:Eu2+ completely after elongating the heating duration to 6 h at 1980°C under 0.5 MPa gas pressure. The same feature was observed under 0.1 MPa gas pressure after firing 8 h at 1750°C. Different heating durations led to different degrees of phase transition.

UR - http://www.scopus.com/inward/record.url?scp=84937974315&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84937974315&partnerID=8YFLogxK

U2 - 10.1111/jace.13646

DO - 10.1111/jace.13646

M3 - Article

AN - SCOPUS:84937974315

VL - 98

SP - 2662

EP - 2669

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

SN - 0002-7820

IS - 8

ER -