Flexural behaviour of post-cured composites at oral-simulating temperatures

C. T. Ho, T. V. Vijayaraghavan, S. Y. Lee, A. Tsai, H. M. Huang, L. C. Pan

研究成果: 雜誌貢獻文章

16 引文 斯高帕斯(Scopus)

摘要

Post-curing treatments have been known to improve the mechanical stability of visible light-cured composites. After individual post-curing treatment, the flexural strength (FS) of four commercial direct/indirect placement composite materials which differ greatly in composition [oligocarbonate dimethacrylate (OCDMA)-based Conquest C & B (CQT), Bisphenol-A glycidyl dimethacrylate (BisGMA)-based Charisma, urethane dimethacrylate (UDMA)-based Concept (CCT), and BisGMA/UDMA-based Dentacolor] was evaluated under water in the temperature range of 12-50°C. A control series was tested in air at room temperature (25 ± 1°C). Data were analysed using ANOVA and Duncan's test. Flexural strengths overall decreased (20-40%, P <0.01) with increasing temperatures except with Conquest C & B. Surprisingly, higher FS values were found in wet conditions than in dry conditions at 25°C. UDMA-based materials much more easily undergo softening in water and by temperature change than do BisGMA- or OCDMA-based materials. Post-cured composites can be significantly affected by exposure to oral environments. Different composition determines the degree of influence.

原文英語
頁(從 - 到)658-667
頁數10
期刊Journal of Oral Rehabilitation
28
發行號7
出版狀態已發佈 - 七月 2001

ASJC Scopus subject areas

  • Dentistry(all)

指紋 深入研究「Flexural behaviour of post-cured composites at oral-simulating temperatures」主題。共同形成了獨特的指紋。

  • 引用此