Flame retardancy effects on intumescent coatings with vinyl acetate copolymers

Chih Shen Chuang, Y. J. Fan, H. J. Sheen

研究成果: 雜誌貢獻文章同行評審

1 引文 斯高帕斯(Scopus)

摘要

This research aimed to study the effects of fire combustion on materials coated with ethylene vinyl acetate and polyvinyl acetate copolymer emulsion resins with differing foam producing substance to dehydrating agent ratios. The flame retardancy of these materials was assessed by evaluating their heat release, CO and CO2 emissions. Experimental results indicate that intumescent paint formulations significantly enhance the flame retardancy of painted plywood, thus reducing peak heat release rate and extending the time to reach peak heat release rate. Moreover, a low amount of foam producing substance enhances the fire retardancy of plywood panels. Furthermore, binder resin containing vinyl acetate monomer in intumescent coatings can enhance fire performance. In addition, low foam producing substance content can form an ideal char layer, which significantly reduces CO and CO2 emissions. The mechanism to achieve more favorable fire performance was verified by carrying out thermogravimetric analysis, which demonstrated lower weight loss. The results of this study provide an improved understanding of the effects of intumescent coatings.
原文英語
頁(從 - 到)541-550
頁數10
期刊International Polymer Processing
34
發行號5
DOIs
出版狀態已發佈 - 十一月 2019

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Polymers and Plastics
  • Industrial and Manufacturing Engineering
  • Materials Chemistry

指紋 深入研究「Flame retardancy effects on intumescent coatings with vinyl acetate copolymers」主題。共同形成了獨特的指紋。

引用此