Fabrication of Mg-Y-Cu bulk metallic glass by mechanical alloying and hot consolidation

P. Y. Lee, W. C. Liu, C. K. Lin, J. C. Huang

研究成果: 雜誌貢獻文章同行評審

15 引文 斯高帕斯(Scopus)

摘要

Mg45Y15Cu40 (numbers indicate at.%) metallic glass powders were prepared by the mechanical alloying of pure Mg, Y, and Cu after 10 h of milling. The thermal stability of these Mg45Y15Cu40 amorphous powders was investigated using the differential scanning calorimeter (DSC). Tg, Tx, and ΔTx are 456, 491, and 35 K, respectively. The as-milled Mg45Y15Cu40 powders were then consolidated by vacuum hot pressing into disk compacts with a diameter and thickness of 10 and 1 mm, respectively. This yielded bulk Mg45Y15Cu40 metallic glass with nanocrystalline precipitates homogeneously embedded in a highly dense glassy matrix. The pressure applied during consolidation can enhance thermal stability and prolong the existence of amorphous phase within Mg45Y15Cu40 powders.
原文英語
頁(從 - 到)1095-1098
頁數4
期刊Materials Science and Engineering A
448-451
DOIs
出版狀態已發佈 - 三月 25 2007
對外發佈

ASJC Scopus subject areas

  • 材料科學(全部)

指紋

深入研究「Fabrication of Mg-Y-Cu bulk metallic glass by mechanical alloying and hot consolidation」主題。共同形成了獨特的指紋。

引用此