Evidence of chemical effect on surface-enhanced Raman scattering of polypyrrole films electrodeposited on roughened gold substrates

研究成果: 雜誌貢獻文章同行評審

104 引文 斯高帕斯(Scopus)

摘要

In this study, polypyrrole (PPy) films were electrochemically deposited on gold substrates roughened by a triangular-wave oxidation-reduction cycle (ORC) in an aqueous solution containing 0.1 N KCl. The results indicate that the intensity of surface-enhanced Raman scattering (SERS) of PPy significantly depends on the ORC scans. Correspondingly, the superficial complex formed on the roughened gold has a strong influence on the SERS effect. The optimum Raman signal of PPy deposited on Au roughened with 25 scans in ORC is ca. 300 times larger than that of PPy deposited on Au without ORC treatment. Meanwhile, the (220) face of Au partly changes into the (111) face with the lowest surface energy after ORC roughening. Toward higher frequency, a shift of C=C backbone stretching of PPy situated at ca. 1575 cm-1 in the SERS spectrum was found which is attributed to interfacial charge transfer from electrodeposited pyrrolylium nitrogen to the roughened gold. Furthermore, this study shows that the SERS enhancement of PPy electropolymerized on roughened Au mainly arises from the chemical effect between PPy and the Au-containing complex.

原文英語
頁(從 - 到)174-181
頁數8
期刊Langmuir
18
發行號1
DOIs
出版狀態已發佈 - 一月 8 2002
對外發佈

ASJC Scopus subject areas

  • 膠體和表面化學
  • 物理與理論化學

指紋

深入研究「Evidence of chemical effect on surface-enhanced Raman scattering of polypyrrole films electrodeposited on roughened gold substrates」主題。共同形成了獨特的指紋。

引用此