Electrochromic properties of nanostructured tungsten oxide films prepared by surfactant-assisted sol-gel process

Ching Lin Wu, Chun Kai Wang, Chung Kwei Lin, Sheng Chang Wang, Jow Lay Huang

研究成果: 雜誌貢獻文章同行評審

27 引文 斯高帕斯(Scopus)

摘要

Pristine and surfactant F-127 added tungsten oxide films have been prepared successfully by sol-gel method using PTA as the precursor sol. After annealing at 300°C, amorphous WO3 films with or without F-127 additions were prepared. The F-127-added tungsten oxide films exhibit porous microstructure, which are affected by the amount of F-127 addition. Nanosized microstructure with pore size less than 10nm can be observed with small amount of F-127 addition (less than 0.06g/ml) , where as larger spherical or tubular pores are found with superfluous F-127 addition (higher than 0.08g/ml). Not only the transmittance modulation but also the coloration efficiency can be improved by adding surfactant F-127. Tungsten oxide film with 0.10g/mlF-127 addition exhibits the best electrochromic performance with a transmittance modulation of 67.6% and a coloration efficiency of 38.3cm2C-1.
原文英語
頁(從 - 到)403-407
頁數5
期刊Surface and Coatings Technology
231
DOIs
出版狀態已發佈 - 九月 25 2013

ASJC Scopus subject areas

  • 化學 (全部)
  • 凝聚態物理學
  • 材料化學
  • 表面、塗料和薄膜
  • 表面和介面

指紋

深入研究「Electrochromic properties of nanostructured tungsten oxide films prepared by surfactant-assisted sol-gel process」主題。共同形成了獨特的指紋。

引用此