Electrochemical and SEM characterization of gold-coated stents in vitro

Chun Che Shih, Chun Ming Shih, Kuang Yi Chou, Shing Jong Lin, Yea Yang Su

研究成果: 雜誌貢獻文章

5 引文 斯高帕斯(Scopus)

摘要

The inert properties of gold make it a useful material for implants. Gold was applied as a coating on 316L stainless steel stents to improve the radiopacity and to provide better thrombogenic resistance and a lower degree of restenosis after deployment. Reports of clinical trials using gold-coated stents showed controversial results. A detailed examination of gold-coated stents was designed to understand the influence of surface conditions on the electrochemical properties in vitro. Corrosion resistance of gold-coated stents was investigated by cyclic polarization, and potentiostatic control. Surface morphologies of gold-coated stents in as-received condition, postinflated condition, and after cyclic polarization were characterized by scanning electron spectroscopy (SES). X-ray mapping identified elemental distribution. Results found severe defects in the gold-coating in the as-received condition, cracks and wrinkles on inflated gold-coated stents, and severe corrosion after cyclic polarization. Leaching of metallic ions in Ringer's solution was possible.
原文英語
期刊Journal of the Electrochemical Society
154
發行號6
DOIs
出版狀態已發佈 - 2007

ASJC Scopus subject areas

  • Electrochemistry
  • Surfaces, Coatings and Films
  • Surfaces and Interfaces

指紋 深入研究「Electrochemical and SEM characterization of gold-coated stents in vitro」主題。共同形成了獨特的指紋。

  • 引用此