Elastic modulus, permeation time and swelling ratio of a new porcine dermal collagen membrane. / Lu, H. K.; Lee, S. Y.; Lin, F. P.
於: Journal of Periodontal Research, 卷 33, 編號 5, 07.1998, p. 243-248.研究成果: 雜誌貢獻 › 文章
}
TY - JOUR
T1 - Elastic modulus, permeation time and swelling ratio of a new porcine dermal collagen membrane
AU - Lu, H. K.
AU - Lee, S. Y.
AU - Lin, F. P.
PY - 1998/7
Y1 - 1998/7
N2 - The goal of a single step therapy has been an important consideration in the development of guided tissue regeneration devices. It would spare the patient from the need for repeated surgery and eliminate many problems associated with a non-resorbable barrier. Animal studies of a collagen membrane extracted from porcine dermis (PDCM), as conditioned by different concentrations of glutaraldehyde (GA), have shown it to be biocompatible and biodegradable (up to 9 wk). This in vitro study further investigated the physical properties of this membrane. A PDCM modified and cross-linked with various concentrations (0.01%, 0.05% and 3.00%) of GA was used. A similar control series was not conditioned. At least 4 specimens for each experimental condition were prepared. The elastic modulus (EM) was measured by a universal testing machine. In the permeability test, Al2O3 particles of different sizes (5-23 μm) were mixed with normal saline to make 5 v/v% suspension and the time needed for collecting 7.5 ml of the filtered suspension from 10 ml suspension was recorded. Swelling ratio (γ) was also measured according to γ = 1/Vf (volume fraction). Data were analysed using ANOVA and Tukey's LSD test. The EM (40.8 ± 3.8 gf/mm2) for the GA conditioned membranes showed no significant difference but was greater (p
AB - The goal of a single step therapy has been an important consideration in the development of guided tissue regeneration devices. It would spare the patient from the need for repeated surgery and eliminate many problems associated with a non-resorbable barrier. Animal studies of a collagen membrane extracted from porcine dermis (PDCM), as conditioned by different concentrations of glutaraldehyde (GA), have shown it to be biocompatible and biodegradable (up to 9 wk). This in vitro study further investigated the physical properties of this membrane. A PDCM modified and cross-linked with various concentrations (0.01%, 0.05% and 3.00%) of GA was used. A similar control series was not conditioned. At least 4 specimens for each experimental condition were prepared. The elastic modulus (EM) was measured by a universal testing machine. In the permeability test, Al2O3 particles of different sizes (5-23 μm) were mixed with normal saline to make 5 v/v% suspension and the time needed for collecting 7.5 ml of the filtered suspension from 10 ml suspension was recorded. Swelling ratio (γ) was also measured according to γ = 1/Vf (volume fraction). Data were analysed using ANOVA and Tukey's LSD test. The EM (40.8 ± 3.8 gf/mm2) for the GA conditioned membranes showed no significant difference but was greater (p
KW - Permeability
KW - Porcine dermal collagen membrane
KW - Swelling ratio
KW - Young's modulus
UR - http://www.scopus.com/inward/record.url?scp=0032109517&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0032109517&partnerID=8YFLogxK
M3 - Article
C2 - 9777590
AN - SCOPUS:0032109517
VL - 33
SP - 243
EP - 248
JO - Journal of Periodontal Research
JF - Journal of Periodontal Research
SN - 0022-3484
IS - 5
ER -