EDM surface characteristics and shape recovery ability of Ti 35.5Ni48.5Zr16 and Ni60Al 24.5Fe15.5 ternary shape memory alloys

S. F. Hsieh, Albert W J Hsue, S. L. Chen, M. H. Lin, K. L. Ou, P. L. Mao

研究成果: 雜誌貢獻文章

14 引文 斯高帕斯(Scopus)

摘要

Electro-discharge craters and recast materials are observed in the electro-discharge machining (EDM) surface of Ti35.5Ni 48.5Zr16 and Ni60Al24.5Fe 15.5 alloys. The recast layer is composed of TiO, NiO, ZrO 2, Fe2O3, Al2O3. The hardening effect near the outer surface for EDMed TiNiZr alloy originates from the surface oxides of the recast layer. The thickness of the recast layer increases upon growing pulse energy. The EDMed Ti35.5Ni 48.5Zr16 alloy still exhibits a good shape recovery, but the shape recovery is slightly reduced due to the depression of the recast layer. The material removal rate (MRR) of Ti35.5Ni 48.5Zr16 alloy is less than that of Ni60Al 24.5Fe15.5 alloy because of the larger θ × kα value. A high discharge energy should have a larger and deeper craters, and a rougher surface. The surface roughness of the EDMed TiNiZr and NiAlFe SMAs is found to obey the empirical equation of Ra = C(IP × τP)β. Having a larger θ × Kα value, Ti35.5Ni48.5Zr16 alloy has a lower Ra value than that of Ni60Al24.5Fe 15.5 alloy after electro-discharge machining.

原文英語
頁(從 - 到)63-68
頁數6
期刊Journal of Alloys and Compounds
571
DOIs
出版狀態已發佈 - 九月 15 2013

ASJC Scopus subject areas

  • Mechanical Engineering
  • Mechanics of Materials
  • Materials Chemistry
  • Metals and Alloys

指紋 深入研究「EDM surface characteristics and shape recovery ability of Ti 35.5Ni48.5Zr16 and Ni60Al 24.5Fe15.5 ternary shape memory alloys」主題。共同形成了獨特的指紋。

  • 引用此