Characterization of Ni57Zr20Ti18Al 5 amorphous powder obtained by mechanical alloying

Pee Yew Lee, Chung Kwei Lin, I. Kuan Jeng, Chien Chung Wang, Giin Shan Chen

研究成果: 雜誌貢獻文章同行評審

7 引文 斯高帕斯(Scopus)

摘要

This study examined the amorphization behavior and thermal stability of mechanically alloyed Ni57Zr20Ti18Al 5 alloy powders synthesized by high-energy ball milling. Complete amorphization is feasible after 5h of milling. The thermal stability of the Ni57Zr20Ti18Al5 amorphous powders was investigated by differential thermal analysis. As the results demonstrated, the temperature interval of the supercooled liquid region defined by the difference between glass transition temperature (Tg) and crystallization temperature (Tx), i.e., ΔT (=T x-Tg) is 54K for Ni57Zr20Ti 18Al5. The glass transition and crystallization temperatures of mechanically alloyed samples are different from those reported in the literature for samples prepared by melt spinning techniques. The different thermal stability is believed to be due to the introduction of impurities into the ball-milled samples during mechanical alloying process. The glass transition behavior in the Ni57Zr20Ti 18Al5 is found to be a kinetically modified thermodynamic phase transformation process.
原文英語
頁(從 - 到)358-362
頁數5
期刊Materials Chemistry and Physics
84
發行號2-3
DOIs
出版狀態已發佈 - 四月 2004
對外發佈

ASJC Scopus subject areas

  • 材料科學(全部)
  • 凝聚態物理學

指紋

深入研究「Characterization of Ni<sub>57</sub>Zr<sub>20</sub>Ti<sub>18</sub>Al <sub>5</sub> amorphous powder obtained by mechanical alloying」主題。共同形成了獨特的指紋。

引用此