Biomimetic synthesis of nacrelike faceted mesocrystals of ZnO-gelatin composite

Yao Hung Tseng, Hsia Yu Lin, Ming Han Liu, Yang Fang Chen, Chung Yuan Mou

研究成果: 雜誌貢獻文章同行評審

89 引文 斯高帕斯(Scopus)

摘要

A fabrication of ZnO hierarchical mesocrystal was achieved by a biomimetic method using gelatin as structuredirecting agent. It was found that the ZnO - gelatin microcrystal with well-defined hexagonal, twin plate shape is built by the slacking of nanoplates. The irregularly edged nanoplates can adjust themselves to each other throughout the microcrystal., resulting in a roughly hexagonal edge. Selected area electron diffraction (SAED) analysis of the ZnO-gelatin microcrystal. demonstrates that all the stacked nanoplates are aligned and oriented to form a single-crystal structure with hexagonal symmetry. The hierarchical structure of ZnO was found to resemble that of naturally occurring nacre. Similar to nacreous architecture, the nanoplate of ZnO was constructed from the oriented attachment of ZnO nanoparticles. More importantly, the lattices of the stacked nanoplates are aligned through minerai, bridges between neighboring plates. A mechanism scheme is proposed for the formation of the gelatin - ZnO hybrid hierarchical structure. The preserved hexagonal shape of the mesocrystal structure consequently results in a whispering gallery mode (WGM) of optical emission where light was confined in the hexagons by total internal reflection. The observation of WGM mode emission in the ZnO hexagon structure shows promises for nanoscale fabrication of optoelectronic devices.

原文英語
頁(從 - 到)18053-18061
頁數9
期刊Journal of Physical Chemistry C
113
發行號42
DOIs
出版狀態已發佈 - 2009
對外發佈

ASJC Scopus subject areas

  • 電子、光磁材料
  • 能源(全部)
  • 物理與理論化學
  • 表面、塗料和薄膜

指紋

深入研究「Biomimetic synthesis of nacrelike faceted mesocrystals of ZnO-gelatin composite」主題。共同形成了獨特的指紋。

引用此