Bioactivity and bone cell formation with poly-ε-caprolactone/bioceramic 3D porous scaffolds

研究成果: 雜誌貢獻文章同行評審

摘要

This study applied poly-ε-caprolactone (PCL), a biomedical ceramic powder as an additive (nano-hydroxyapatite (nHA) or β-tricalcium diphosphate (β-TCP)), and sodium chloride (NaCl) and ammonium bicarbonate ((NH4)HCO3) as porogens; these stuffs were used as scaffold materials. An improved solvent-casting/particulate-leaching method was utilized to fabricate 3D porous scaffolds. In this study we examined the physical properties (elastic modulus, porosity, and contact angle) and degradation properties (weight loss and pH value) of the 3D porous scaffolds. Both nHA and β-TCP improved the mechanical properties (elastic modulus) of the 3D porous scaf-folds. The elastic modulus (0.15~1.865 GPa) of the various composite scaffolds matched that of human cancellous bone (0.1~4.5 GPa). Osteoblast-like (MG63) cells were cultured, a microculture te-trazolium test (MTT) was conducted and alkaline phosphatase (ALP) activity of the 3D porous scaffolds was determined. Experimental results indicated that both nHA and β-TCP powder improved the hydrophilic properties of the scaffolds. The degradation rate of the scaffolds was accelerated by adding nHA or β-TCP. The MTT and ALP activity tests indicated that the scaffolds with a high ratio of nHA or β-TCP had excellent properties of in vitro biocompatibility (cell attachment and prolifer-ation).

原文英語
文章編號2718
期刊Polymers
13
發行號16
DOIs
出版狀態已發佈 - 八月 2021

ASJC Scopus subject areas

  • 化學 (全部)
  • 聚合物和塑料

指紋

深入研究「Bioactivity and bone cell formation with poly-ε-caprolactone/bioceramic 3D porous scaffolds」主題。共同形成了獨特的指紋。

引用此