Aqueous Li+/Al3+ alkaline solution for CO2 capture and the massive Li-Al-CO3 hydrotalcite precipitation during the interaction between CO2 gas and the Li+/Al 3+ aqueous solution

Meng Chang Lin, Fu Tsung Chang, Jun Yen Uan

研究成果: 雜誌貢獻文章同行評審

13 引文 斯高帕斯(Scopus)

摘要

The concentrations of Al3+ and Li+ in an aqueous alkali affect the ability of the solution to capture CO2. When CO2 gas was forced into such a solution, CO2 was captured via the formation of a carbonate-containing compound. The carbonate-containing compound was Li-Al-CO3 hydrotalcite (Li-Al-CO3 LDH) or amorphous aluminium hydroxycarbonate. The former compound contained 2.84-3.22 wt% carbon, while the latter contained less carbon (1.52-1.97 wt%). The Li-Al-CO3 LDH was porous with nanosized pores and had a BET surface area of 114.8-161.8 m2 g-1. The injection of a relatively low CO2 gas flow rate into the Al3+- and Li +-containing aqueous solution favoured the production of Li-Al-CO3 LDH. For example, forcing CO2 gas into the aqueous solution at a flow rate of 70 mL min-1 produced Li-Al-CO 3 LDH. Injecting CO2 at a higher flow rate (120 mL min-1) into the same solution produced amorphous aluminium hydroxycarbonate. A CO2 capture capacity (mmol per gram AlLi IMC) of up to ∼30 mmol g-1 (1.30 kg CO2 per kg of AlLi) was achieved in 120 s. The fall in the pH of the alkaline solution during CO 2 bubbling was the critical factor that determined whether the final product was Li-Al-CO3 LDH or amorphous aluminum hydroxycarbonate.
原文英語
頁(從 - 到)14773-14782
頁數10
期刊Journal of Materials Chemistry A
1
發行號46
DOIs
出版狀態已發佈 - 12月 14 2013
對外發佈

ASJC Scopus subject areas

  • 化學 (全部)
  • 可再生能源、永續發展與環境
  • 材料科學(全部)

指紋

深入研究「Aqueous Li+/Al3+ alkaline solution for CO2 capture and the massive Li-Al-CO3 hydrotalcite precipitation during the interaction between CO2 gas and the Li+/Al 3+ aqueous solution」主題。共同形成了獨特的指紋。

引用此