An operando X-ray diffraction study of chloroaluminate anion-graphite intercalation in aluminum batteries

Chun Jern Pan, Chunze Yuan, Guanzhou Zhu, Qian Zhang, Chen Jui Huang, Meng Chang Lin, Michael Angell, Bing Joe Hwang, Payam Kaghazchi, Hongjie Dai

研究成果: 雜誌貢獻文章同行評審

74 引文 斯高帕斯(Scopus)

摘要

We investigated rechargeable aluminum (Al) batteries composed of an Al negative electrode, a graphite positive electrode, and an ionic liquid (IL) electrolyte at temperatures down to −40 °C. The reversible battery discharge capacity at low temperatures could be superior to that at room temperature. In situ/operando electrochemical and synchrotron X-ray diffraction experiments combined with theoretical modeling revealed stable AlCl4 −/graphite intercalation up to stage 3 at low temperatures, whereas intercalation was reversible up to stage 4 at room temperature (RT). The higher-degree anion/graphite intercalation at low temperatures affords rechargeable Al battery with higher discharge voltage (up to 2.5 V, a record for Al battery) and energy density. A remarkable cycle life of >20,000 cycles at a rate of 6C (10 minutes charge time) was achievable for Al battery operating at low temperatures, corresponding to a >50-year battery life if charged/discharged once daily.
原文英語
頁(從 - 到)5670-5675
頁數6
期刊Proceedings of the National Academy of Sciences of the United States of America
115
發行號22
DOIs
出版狀態已發佈 - 5月 29 2018
對外發佈

ASJC Scopus subject areas

  • 多學科

指紋

深入研究「An operando X-ray diffraction study of chloroaluminate anion-graphite intercalation in aluminum batteries」主題。共同形成了獨特的指紋。

引用此