Alumina-promoted mesoporous sulfated zirconia: A catalyst for n-butane isomerization

Jung Hui Wang, Chung Yuan Mou

研究成果: 雜誌貢獻文章同行評審

52 引文 斯高帕斯(Scopus)

摘要

Mesoporous sulfated zirconia (MP-ZrO2) were synthesized hydrothermally using Zr(O-nPr)4 as zirconium precursor, ammonium sulfate as sulfur source and CTABr as template. Then the as-synthesized mesoporous materials were directly impregnated with aluminum sulfate to give the acidic Al-promoted mesoporous sulfated zirconia. (AS/MP-ZrO2). The AS/MP-ZrO2 catalyst was characterized by nitrogen physisorption (BET) for texture properties, by X-ray diffraction (XRD) for confirming the phase and by TEM for particle sizes. The catalytic conversion of n-butane isomerization was measured in a flow reactor. With the addition of a proper amount of aluminum as a promoter, the catalytic behavior for n-butane isomerization at low temperature in flow system was strongly promoted. The increase of activity was determined primarily by the amount of alumina addition and by the temperature of calcination. The highest catalytic performance is for the catalyst prepared at an optimum 3 mol.% Al loading and calcination at 650°C. The nature of the acidic sites was determined by X-ray photoelectron spectroscopy (XPS) measurements of N 1 s of the adsorbed pyridine. Three kinds of acid sites were identified on the catalyst: a Lewis site, a weak Brønsted site and a strong Brønsted site. The catalytic activities are correlated with the amount of weak Brønsted acid sites. The remarkable activity and stability of the Al-promoted catalysts are due to a balanced distribution of acid sites strength with an enhanced amount of weak Brønsted acid sites.

原文英語
頁(從 - 到)128-136
頁數9
期刊Applied Catalysis A: General
286
發行號1
DOIs
出版狀態已發佈 - 5月 26 2005
對外發佈

ASJC Scopus subject areas

  • 催化
  • 製程化學與技術

指紋

深入研究「Alumina-promoted mesoporous sulfated zirconia: A catalyst for n-butane isomerization」主題。共同形成了獨特的指紋。

引用此