Preparation and characterization of nanocrystalline Nb 3Al alloy

Chuan Yi Wu, Hong Ming Lin, Hsin Fu Lin, Ming Fong Tai, Chang Ren Wang, Chung Kwei Lin, P. Y. Lee

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

The nanocrystalline Nb 3Al is prepared by the gas condensation method. The nanocrystalline Nb 3Al size with injected 0.1 mbar helium pressure is about 15nm. During the gas condensation process, the superconductivity disappears at as-prepared NC Nb 3Al with the mean particle size about 15 nm. After annealing the as-prepared NC Nb 3Al at 500°C for 30 minutes, the mean particle size of NC Nb 3Al is about 30 nm and the superconductivity appear with T c about 16K. The results show that superconductivity can be achieved in nanocrystals with a rather smaller size than the typical penetration length of magnetic field. Further study of the influence of gas condensation alloying at high magnetic fields is crucial to the understanding of the superconductivity properties of NC Nb 3Al.

Original languageEnglish
Pages (from-to)1967-1971
Number of pages5
JournalScripta Materialia
Volume44
Issue number8-9
DOIs
Publication statusPublished - May 18 2001
Externally publishedYes

    Fingerprint

Keywords

  • Gas condensation method
  • Nanocrystalline Nb Al
  • Superconductivity
  • XRD

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Materials Science(all)
  • Metals and Alloys

Cite this

Wu, C. Y., Lin, H. M., Lin, H. F., Tai, M. F., Wang, C. R., Lin, C. K., & Lee, P. Y. (2001). Preparation and characterization of nanocrystalline Nb 3Al alloy. Scripta Materialia, 44(8-9), 1967-1971. https://doi.org/10.1016/S1359-6462(01)00833-8