Characteristics of the ring stretching of oxidized polypyrrole on the surface-enhanced Raman spectrum

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

In this study, polypyrrole (PPy) films were electropolymerized under different preparation conditions on rough gold substrates. The peak shown at the higher frequency of the double peaks at about 1329 and 1386 cm-1 in surface-enhanced Raman scattering of PPy was initially assigned to the ring stretching of oxidized PPy. A systematic study was carried out to confirm this assignment. It was found that the conductivity of PPy was strongly related to and increased with this Raman peak intensity of oxidized PPy. Meanwhile, the normalized relative intensities of this Raman peak for various PPy films are consistent with their corresponding doping levels.

Original languageEnglish
Pages (from-to)490-493
Number of pages4
JournalJournal of Solid State Electrochemistry
Volume6
Issue number7
DOIs
Publication statusPublished - Sep 2002
Externally publishedYes

Fingerprint

polypyrroles
Polypyrroles
Stretching
Raman scattering
Raman spectra
rings
Gold
polypyrrole
Doping (additives)
gold
conductivity
preparation
Substrates

Keywords

  • Conductivity
  • Oxidized polypyrrole
  • Surface-enhanced Raman scattering

ASJC Scopus subject areas

  • Electrochemistry

Cite this

@article{a73cc993beb746b18c4449673eed0c50,
title = "Characteristics of the ring stretching of oxidized polypyrrole on the surface-enhanced Raman spectrum",
abstract = "In this study, polypyrrole (PPy) films were electropolymerized under different preparation conditions on rough gold substrates. The peak shown at the higher frequency of the double peaks at about 1329 and 1386 cm-1 in surface-enhanced Raman scattering of PPy was initially assigned to the ring stretching of oxidized PPy. A systematic study was carried out to confirm this assignment. It was found that the conductivity of PPy was strongly related to and increased with this Raman peak intensity of oxidized PPy. Meanwhile, the normalized relative intensities of this Raman peak for various PPy films are consistent with their corresponding doping levels.",
keywords = "Conductivity, Oxidized polypyrrole, Surface-enhanced Raman scattering",
author = "Liu, {Yu Chuan}",
year = "2002",
month = "9",
doi = "10.1007/s10008-001-0262-3",
language = "English",
volume = "6",
pages = "490--493",
journal = "Journal of Solid State Electrochemistry",
issn = "1432-8488",
publisher = "Springer Verlag",
number = "7",

}

TY - JOUR

T1 - Characteristics of the ring stretching of oxidized polypyrrole on the surface-enhanced Raman spectrum

AU - Liu, Yu Chuan

PY - 2002/9

Y1 - 2002/9

N2 - In this study, polypyrrole (PPy) films were electropolymerized under different preparation conditions on rough gold substrates. The peak shown at the higher frequency of the double peaks at about 1329 and 1386 cm-1 in surface-enhanced Raman scattering of PPy was initially assigned to the ring stretching of oxidized PPy. A systematic study was carried out to confirm this assignment. It was found that the conductivity of PPy was strongly related to and increased with this Raman peak intensity of oxidized PPy. Meanwhile, the normalized relative intensities of this Raman peak for various PPy films are consistent with their corresponding doping levels.

AB - In this study, polypyrrole (PPy) films were electropolymerized under different preparation conditions on rough gold substrates. The peak shown at the higher frequency of the double peaks at about 1329 and 1386 cm-1 in surface-enhanced Raman scattering of PPy was initially assigned to the ring stretching of oxidized PPy. A systematic study was carried out to confirm this assignment. It was found that the conductivity of PPy was strongly related to and increased with this Raman peak intensity of oxidized PPy. Meanwhile, the normalized relative intensities of this Raman peak for various PPy films are consistent with their corresponding doping levels.

KW - Conductivity

KW - Oxidized polypyrrole

KW - Surface-enhanced Raman scattering

UR - http://www.scopus.com/inward/record.url?scp=0035982353&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035982353&partnerID=8YFLogxK

U2 - 10.1007/s10008-001-0262-3

DO - 10.1007/s10008-001-0262-3

M3 - Article

AN - SCOPUS:0035982353

VL - 6

SP - 490

EP - 493

JO - Journal of Solid State Electrochemistry

JF - Journal of Solid State Electrochemistry

SN - 1432-8488

IS - 7

ER -